HOME / 친환경분해수지 / TRIOZ-기술자료

(주)알커미스는 친환경 화학소재 전문기업입니다.

산화-생분해 원리

Indoor Testing ( Thermal & Ultraviolet )

Thermal Degradation - Mechanical Strength

Thermal Degradation
  • Equipment (Model) : LT-DO 72
  • Temperature : 80 deg.C
  • Sample thickness : 40 ~ 50 micron
  • 0h ~ 168h (7 days)
Mechanical Strength (UTM)
  • Up to 168h measured

Thermal Degradation – Molecular Weight

  Mn (dalton) Mw (dalton) Mw/Mn
24h 10,272 85,772 8.35
48h 5,370 31,629 5.89
72h 2,320 8,515 3.67
120h 1,620 4,973 3.07
168h 1,196 3,564 2.98

UV Degradation – Mechanical Strength

UV Degradation
  • Equipment (Model) : UV lamp aging tester (KL-LUV-1)
  • Lamp Wavelength : 290 – 400 nm
  • Sample Thickness : 40~50 micron
  • 0h to 350h (14.6 days)
Mechanical Strength (UTM)
  • Up to 350h measured
  • Above 200h Unable to measure

Thermal Degradation – Molecular Weight

  Mn (dalton) Mw (dalton) Mw/Mn
50h 10,566 85,679 8.11
100h 6,144 34,981 5.69
150h 3,495 16,772 4.8
200h 4,561 14,678 4.12
250h 2,489 9,171 3.68
300h 2,184 6,901 3.16
350h 1,648 4,625 3.26

Biodegradability

“KS M ISO 14855-1 : 2013” @ FITI 시험연구원

퇴비화 조건에서 플라스틱 재료의 호기적 생분해도 측정:
이산화탄소 분석에 의한 방법 - 시료를 적정법으로 생분해도를 측정
산화 생분해 촉매 함유 플라스틱 제품에 포함된 유기탄소중 30%는 1.5개월 이내 이산화탄소로 전환

Heavy Metal Test

Item 허용치 TRIOZ
Unit mg/kg mg/kg
Zn 150 19
Cu 50 13
Ni 25 N/D
Cd 0.5 N/D
Pb 50 2
Hg 0.5 N/D
Cr 50 31
Mo 1 N/D
Se 0.75 -
As 5 N/D
F 100 -

N/D : Not Detected

1) 중금속 함유량 측정 기관 및 방법
- 분석기관 : KTC
- 방법 : KS M 0032 : 2009

2) 측정 결과
- 모든 요소 중금속의 함유량 허용치 내에서 검출

자연환경 옥외 폭로 테스트
(건설생활환경시험연구원 서산 옥외 시험장)

시험 전
1개월 후
2개월 후
3개월 후
※ 옥외(직접)폭로 기간 중 기상정보

- 폭로 각도 : 45°, - 기온 : 최대(33.4) ℃, 최소(14.0) ℃, 평균(23.7) ℃
- 상대습도 : 최대(96) %, 최소(11) %, 평균(66) %,
- 총 일사량(305 ~ 2 800) nm : 1 600.42 MJ/m2 / 총 자외선 량(315 ~ 400) nm : 89.01 MJ/m2